- Research article
- Open Access
Diffraction evidence for the structure of cellulose microfibrils in bamboo, a model for grass and cereal celluloses
BMC Plant Biology volume 15, Article number: 153 (2015)
Cellulose from grasses and cereals makes up much of the potential raw material for biofuel production. It is not clear if cellulose microfibrils from grasses and cereals differ in structure from those of other plants. The structures of the highly oriented cellulose microfibrils in the cell walls of the internodes of the bamboo Pseudosasa amabilis are reported. Strong orientation facilitated the use of a range of scattering techniques.
Small-angle neutron scattering provided evidence of extensive aggregation by hydrogen bonding through the hydrophilic edges of the sheets of chains. The microfibrils had a mean centre-to-centre distance of 3.0 nm in the dry state, expanding on hydration. The expansion on hydration suggests that this distance between centres was through the hydrophilic faces of adjacent microfibrils. However in the other direction, perpendicular to the sheets of chains, the mean, disorder-corrected Scherrer dimension from wide-angle X-ray scattering was 3.8 nm. It is possible that this dimension is increased by twinning (crystallographic coalescence) of thinner microfibrils over part of their length, through the hydrophobic faces. The wide-angle scattering data also showed that the microfibrils had a relatively large intersheet d-spacing and small monoclinic angle, features normally considered characteristic of primary-wall cellulose.
Bamboo microfibrils have features found in both primary-wall and secondary-wall cellulose, but are crystallographically coalescent to a greater extent than is common in celluloses from other plants. The extensive aggregation and local coalescence of the microfibrils are likely to have parallels in other grass and cereal species and to influence the accessibility of cellulose to degradative enzymes during conversion to liquid biofuels
Cellulose comprises long microfibrils, each a few nm in diameter and containing some tens of glucan chains. The structure of cellulose microfibrils, partially crystalline and partially disordered, is not fully known . Cellulose from cereal crop residues and from grasses like Miscanthus is a sustainable starting point for biofuels  and, increasingly, for bio-based chemical manufacturing . The conversion of cellulose to useful products can be achieved by enzymatic depolymerisation  and is inhibited by lignification, by incompletely understood features of microfibril structure and by aggregation of the microfibrils [5,6].
Evidence has emerged, first from 13C NMR spectroscopy [7-9] and more recently from other spectroscopic and scattering technologies [10-15], for partially ordered cellulose microfibrils no more than about 3 nm in diameter. Cellulose microfibrils of that size have been reported from unlignified primary cell walls [13,15] and from gymnosperm xylem, which is dominated by lignified secondary cell walls [7,10,16], although cotton, flax and certain other materials composed of relatively pure cellulose contain thicker microfibrils [14,17,18]. A 3 nm microfibril is too thin to accommodate the 36 chains formerly assumed to be present in microfibrils emerging from the 6-membered ‘rosette’ responsible for cellulose biosynthesis . Recently, based on spectroscopic and scattering evidence, partially ordered 18- and 24-chain models have been suggested for mung bean, celery and spruce wood cellulose [10,13,15]. In primary cell walls, microfibrils of approximately this size may be stacked or ‘twinned’ along part of their length, cohering through the hydrophobic  crystal face so that the mean lateral dimension is slightly increased in that direction [15,20]. An 18-chain microfibril model with some ‘twinning’ of this nature appeared to fit the X-ray and NMR data for mung bean primary-wall cellulose . It is not clear whether similar microfibril structures are present in grass and cereal celluloses dominated by lignified secondary walls, for which the most detailed recent model is the flattened-hexagonal, 36-chain structure proposed on AFM evidence for the cellulose of corn stover .
It would therefore be of interest to examine the structure of cellulose microfibrils in a grass or cereal species, using the scattering methods that have led to models with less than 36 chains for the microfibrils of non-graminaceous plants. A technical problem is that some of these methods require very well-oriented microfibrils . Highly uniform cellulose orientation is not a well-established feature of most grass and cereal tissues. Bamboo cellulose, however, is particularly well-oriented [21,22]. This feature is responsible for the high stiffness of some bamboo species , and its adoption as an engineering material both as intact canes and as the fibre component in biocomposites . In other respects bamboos are typical, if overgrown, grasses [24,25]. Here we report evidence for cellulose microfibril structure in the commercially important bamboo species Pseudosasa amabilis (Tonkin cane).
Wide-angle X-ray scattering (WAXS)
Intact internode tissue from mature bamboo stems gave a well-oriented fibre diffraction pattern (Figs. 1a and a). In the azimuthal direction it was possible to dissect the orientation distribution into a wide and a narrow component (Fig. 1a), corresponding perhaps to different cell-wall layers  or to different cell types within the vascular bundles. In the radial direction, the background-corrected equatorial profile obtained with Cu Kα radiation is shown in Fig. 1c. It resembled that observed  for bamboo cellulose and had some similarities to the corresponding profile for spruce wood . However the 200 reflection was narrower and at slightly lower q than for spruce wood implying a mean intersheet spacing (0.403 nm +/− 0.001 nm from three diffraction patterns using both Cu and Mo radiation) about 3 % wider than in spruce cellulose. The 1–10 and 110 reflections were strongly overlapped, implying a smaller monoclinic angle than in wood or in the published cellulose Iβ structure . The mean best-fit monoclinic angle was 92°, although this parameter was difficult to estimate because broadening and overlap of the 1–10 and 110 reflections made them hard to distinguish from one another. The wide intersheet spacing and small monoclinic angle match the observations of Driemeier et al.  on sugar cane cellulose.
Wide intersheet spacing and a small monoclinic angle are features normally associated with primary-wall celluloses [13,15,28], but the radial width of the equatorial reflections from bamboo cellulose was considerably less than has been observed from primary-wall celluloses, indicating either greater crystallite dimensions or less disorder. Separating the disorder-related and size-related components of broadening as described by [10,14] gave a Scherrer dimension (mean column length) of 3.84 nm ± 0.13 nm (n = 3) perpendicular to the  lattice plane and a value of 0.036 ± 0.001 for the disorder parameter g. This value of g is in agreement with other cellulosic materials but the Scherrer dimension is greater than was found for spruce wood or primary-wall cellulose [10,14]. The  Scherrer dimension calculated here was also greater than was estimated previously for bamboo cellulose , as expected because of the allowance made here for disorder-related broadening. Broadening of the 1–10 and 110 reflections was difficult to quantify because of the strong overlap between them and because their broadening appeared to be less asymmetric than that of the 200 reflection. With the best-fit value of the monoclinic angle they were clearly substantially wider at half height than the 200 reflection, implying shorter dimensions and/or higher disorder in these crystallographic directions.
An unusual feature of the equatorial scattering profile from this well-oriented bamboo cellulose was the presence of a weak 100 shoulder close to q = 8 nm−1, which might indicate an anomaly in intersheet stagger, or the spacing between alternate sheets of chains exposed at a  face of the microfibril.
Wide-angle neutron scattering (WANS)
Wide-angle neutron scattering patterns were recorded from bamboo with and without prior equilibration with D2O to exchange surface hydroxyl groups. In cellulose Iβ, complete deuteration (which requires much more extreme conditions) slightly increases the relative intensity of the 200 reflection and greatly decreases the relative intensity of the 1–10 reflection . Since the cellulose Iβ lattice is too close-packed to be permeable to H2O or D2O, any difference between the H and D diffraction patterns (Fig. 2) may be concluded to be derived from hydroxyl groups that were accessible to D2O and located either at the surface of the microfibrils, or in disordered internal regions, or in any hemicellulose segments that might be ordered enough to adopt the same chain conformation as cellulose.
The 200 reflection was at essentially the same position before and after deuteration, so that the difference diffraction pattern (Fig. 2) showed only the increase in intensity. The width of the 200 reflection was slightly less than was observed by WAXS implying, if anything, a slightly greater Scherrer dimension perpendicular to the sheets of chains. However the absence of a 400 reflection with measureable intensity in WANS prevented the calculation of a disorder correction.
The negative value of the 1–10 reflection (q = 11 nm−1) in the D-H difference diffraction pattern allowed its position to be established and differentiated from the overlapping 110 reflection. Fitting the H and D diffraction patterns on the hypothesis that the 1–10 and 110 reflections were unaltered in q by deuteration, the best-fit spacing implied a monoclinic angle of 94°, in reasonable agreement with the best-fit value of the monoclinic angle from WAXS. The equatorial part of the WANS pattern was thus consistent with the same lateral d-spacings for the domains accessible to deuteration as for the inaccessible domains, implying a surface location for the majority of the deuteration. D2O-accessible regions within the microfibrils, if abundant, would require looser chain packing which was not observed.
The signal:noise ratio in WANS was insufficient for the 100 reflection to be distinguished. On the fibre axis, the 001 and 002 reflections were observed only after deuteration (Fig. 2b), implying that there was some irregularity in the longitudinal stagger of the accessible chains exposed at the surfaces of the microfibrils.
Small-angle neutron scattering (SANS)
When cellulose microfibrils aggregate together with any regularity, Bragg scattering (diffraction) at small angles can be observed from the arrayed microfibrils themselves, in addition to the wide-angle scattering from the crystal planes within the microfibrils . In woody materials if the microfibrils are in close contact, there will be insufficient matrix material between them to provide the contrast for small-angle Bragg scattering of X-rays. However if the microfibrils can be forced apart by D2O there is intense neutron scattering contrast between the D2O and the cellulose, as can be seen at low q in Fig. 2a. Starting from bamboo saturated with D2O, the D2O content was progressively reduced to zero in the absence of H2O. Considerable SANS contrast remained at zero D2O content (Fig. 3a) due to exchange of hydroxyl groups on cellulose surfaces  or hemicelluloses. As the D2O content was reduced the small-angle Bragg peak moved to higher q, implying that on drying the nominal centre-to-centre spacing of the microfibrils narrowed from 3.19 nm at 25 % D2O to 2.96 nm at 0 % D2O (Fig. 3c). It may be assumed that the centre-to-centre spacing at 0 % D2O corresponds to microfibrils touching one another and is therefore equal to the microfibril diameter. After drying the remaining deuterium atoms were on hydroxyl groups, not water molecules. It is therefore likely that it was contact through the hydrophilic faces of the microfibrils that gave rise to the small-angle Bragg scattering, not through the 200 faces suggested as the sites of microfibril coalescence (twinning).
No small-angle Bragg peak was observed from bamboo equilibrated with 35 % D2O: 65 % H2O. A mixture of D2O and H2O in these proportions matches the cellulose scattering length density and thus gives zero contrast between the liquid phase and cellulose . This observation showed that the spacing observed was indeed between cellulose microfibrils, not lignin or some other feature of the cell-wall structure of bamboo, such as arabinoxylans. The d-spacings shown in Fig. 3b do not necessarily correspond to any form of global mean, because the scattering contrast is likely to be greatest when the microfibrils are just far enough apart to permit D2O to enter between them: wider spacings are probably too irregular for strong Bragg scattering. The Bragg peaks observed in D2O were broad, indicating that only a few microfibrils were packed laterally together, or that the packing was disordered, or most probably both.
The wide-angle and small-angle scattering patterns and NMR spectra for bamboo cellulose resembled those from wood and dicot primary cell walls in many respects, but there were interesting differences. Although bamboo internodes can certainly be called woody, with secondary wall layers and strong lignification  the unit cell parameters of the crystalline cellulose fraction resembled those of primary cell walls, with a small monoclinic angle and relatively large intersheet  d-spacing. Essentially the same intersheet d-spacing was measured by neutron scattering when the accessible cellulose chains were deuterated. This observation strongly suggests that most of the D2O-accessible cellulose chains were at the microfibril surface rather than buried in the interior, since the chain packing appeared to be as tight as in other crystalline celluloses into which water cannot penetrate.
The diameters of cellulose microfibrils have often been estimated on the assumption that they are approximately as wide as they are high , although the AFM study of Ding and Himmel  suggested that maize primary-wall microfibrils were about 3 nm high perpendicular to the  plane and 3.6 nm wide parallel to the  plane. The different techniques used here provide information on microfibril dimensions in each lateral direction. The Scherrer dimension obtained by WAXS after disorder correction was 3.8 nm perpendicular to the  plane, and the WANS data implied that 3.8 nm was not an overestimate in this direction. Bamboo microfibrils, therefore, are substantially larger in this dimension, on average, than microfibrils of softwood  or dicot primary-wall cellulose [13,15]. The WAXS data suggested smaller lateral dimensions in other directions, but this inference was not quantitative because the disorder correction was difficult to apply to broadening of the 1–10 and 110 reflections. The mean centre-to centre distance of 3.0 nm, estimated from the position of the SANS coherent scattering peak, must include hydrogen-bonding cellulose surfaces that deuterate to provide the SANS contrast. This distance cannot therefore be perpendicular to the  plane; it could be parallel or diagonal to that plane depending on which crystal faces form the boundaries of the microfibril. A mean sheet width of three chains, giving a mean dimension of about 3 nm in that direction, would be consistent with the WAXS data on the assumption that there was substantial disorder at the hydrophilic faces of the microfibril Fig. 4.
A cellulose chain within the Iβ crystal structure occupies 0.32 nm2 in cross-section  or 0.33 nm2 with the slightly larger d-spacings found for bamboo. This cross-sectional area would suggest that the observed microfibril dimensions, 3.8 nm perpendicular to the sheets of chains and 3.0 nm across the sheets, would allow space for about 34 chains. However the irregular hydrophilic surfaces of the microfibrils mean that fewer chains can be fitted within these overall dimensions. Based on microfibril models similar to those suggested for spruce cellulose  the number of chains would be about 26–30 depending on the detailed shape of the microfibrils. That would be consistent with the 18-chain model proposed for mung bean primary-wall cellulose  only if there were a much greater extent of ‘stacking’ or ‘twinning’ in which two 18-chain microfibrils coalesce through the  faces for part of their length. The suggested dimensions and this pattern of coalescence and divergence recall the AFM observations by Ding and Himmel  on the microfibrils of maize primary cell walls, but with the crystal lattice turned through 90°. AFM methods give no indication of the orientation of the lattice planes. It should be stressed that only averaged dimensions can be derived from our data, and the dimension obtained by SANS is not a true average. The data of Wang et al.  on local crystallographic variability between bamboo cell walls, the developmental variation in maize recorded by Zhang et al.  and the intricate aggregation of maize microfibrils imaged by Ding and Himmel , show that averaged dimensions may conceal complex local patterns of variation. The ‘twinning’ or ‘stacking’ (crystallographic coalescence) phenomenon proposed by Newman et al.  and Thomas et al.  may be sufficient to provide a large part of this variation without assuming heterogeneity in the structures of microfibrils extruded by the terminal complexes that carry out their biosynthesis .
Aggregation of cellulose microfibrils in bamboo and in other monocotyledonous species [19,22] appears to involve contact with and without crystalline coalescence. How such aggregation interferes with the access of cellulases to the cellulose surfaces that they attack, and how chemical pretreatments impact on the extent of microfibril aggregation , are questions that deserve closer attention during the development of enzymatic processes for manufacturing biofuels and bio-based materials from grass and cereal biomass.
The microfibrils of bamboo cellulose, although derived mainly from secondary cell walls, resembled the primary-wall celluloses of other plants in having relatively wide inter-sheet spacing and small monoclinic angle. The mean microfibril diameter was 3.8 nm perpendicular to the sheets of chains, unusually large for a woody material but consistent with fusion of pairs of smaller microfibrils over part of their length. The bamboo microfibrils were also loosely aggregated into bundles with a limited degree of regularity in spacing. D2O was able to penetrate into the microfibril bundles, increasing the microfibril spacing as hydration progressed.
Tonkin cane (Pseudosasa amabilis) internodes were split and the interior removed to leave strips of the outer tissue approximately 2 mm wide × 1 mm deep.
Small-angle neutron scattering (SANS)
SANS analysis was conducted on the high-flux beamline D33 at the Institut Laue-Langevin (ILL), Grenoble. The neutron beam had a wavelength λ = 3.5 Å with spread Δλ/λ = 10 %, and was passed through a 2.8 m long collimator tube. Sample-to-detector distance was 2 m. The q range covered in this experiment extended from 0.4 nm−1 to 2.8 nm−1. A number of bamboo segments about 1 mm thick were placed side by side to give a sheet wider than the beam diameter. The bamboo segments were saturated with H2O, D2O or 35:65 D2O:H2O, the contrast match composition for cellulose, and then equilibrated with phosphorus pentoxide to dry to a predetermined weight. The samples were immediately sealed in an aluminium foil package 15 mm square. At least 1 h was then allowed for internal equilibration of moisture . An empty foil container was used as background.
Wide-angle X-ray scattering (WAXS)
X-ray diffraction patterns were obtained at ambient temperature using a Rigaku R-axis/RAPID image plate diffractometer. Both Cu Kα (λ = 0.15406 nm, one sample) and Mo (λ = 0.7071 nm, two samples) sources were used, with the beam collimated to a diameter of 0.5 mm. Scattering angles were expressed as q = 4πsinθ/λ. Samples were 1 mm thick in the direction parallel to the beam and their other dimensions exceeded the beam diameter. The diffraction patterns were collected in perpendicular transmission mode. Radial profiles of scattered intensity I as a function of q were integrated over azimuthal angles of 2° using the AreaMax software package (Rigaku/MSC, Tokyo). Background correction was carried out as described . Each tangential profile was fitted by a dual Gaussian function and the narrower of the two Gaussians was used to reconstruct the equatorial radial profile . In the radial direction, the overlapping 1–10 and 110 reflections were fitted by two Gaussian functions and the 200 reflection was fitted by an asymmetric function F(q) constructed as follows: when q > the point of maximum intensity q 0, F(q) = F 0(q), a simple Gaussian function. When q < q 0, F(q) = F 0(q)(1 + 0.1(q - q 0)2). It was assumed that the integral width δq of F 0(q) was controlled by both disorder and the column length of the crystallite, so that δq = δq 0 + π/2 g 2 q 2 d, where g is the non-asymmetric disorder parameter and d is the lattice spacing. Then a plot of integral width δq against q 2 d is linear with, at the intercept, the Scherrer dimension (mean column length) L = 2π/δq 0 .
Wide-angle neutron scattering (WANS)
Bamboo samples were prepared as for SANS at 25 % H2O or D2O content, sufficient to saturate the cell walls without filling the cell lumina. WANS analysis was conducted on beamline D19 at the ILL. Beamline D19 has a four-circle diffractometer with a cylindrical detector consisting of a 256 × 640 array of gas-filled cells giving an aperture 30° vertically × 120° horizontally. The neutron beam was monochromated to a wavelength of 2.42 Å and the sample-to-detector distance, taken to the electrode plane in each cell at the equator, was 756 mm. The response for each cell of the detector was calibrated using the isotropic incoherent neutron scattering from a vanadium rod, and blank-corrected using an empty aluminium foil container.
The absorption coefficient of the sample along the beam axis was calculated from absorption coefficients based on the elemental composition. Absorption factors at all angles within the aperture of the detector were then calculated using in-house software based on the integrated path length through the sample, which was assumed to have cuboidal geometry and was wider than the neutron beam. The fibre axis was tilted such that the full widths of the 001, 002, 003 and 004 reflections were collected. In-house software was then used to reconstruct the data into reciprocal space and to join together the component images of the diffraction pattern. The combined images were exported into Fit2D, where radial intensity profiles integrated over 10° in azimuth were calculated in the equatorial and meridional directions.
Nuclear Magnetic Resonance
Wide-angle X-ray Scattering
Wide-angle Neutron Scattering
Small-angle Neutron Scattering
Atomic Force Microscopy
- gg :
- gt :
- tg :
Nishiyama Y, Johnson GP, French AD, Forsyth VT, Langan P. Neutron crystallography, molecular dynamics, and quantum mechanics studies of the nature of hydrogen bonding in cellulose I-beta. Biomacromolecules. 2008;9:3133–40.
Carroll A, Somerville C. Cellulosic biofuels. Annu Rev Plant Biol. 2009;60:165–82.
Klemm D, Kramer F, Moritz S, Lindstrom T, et al. Nanocelluloses: a new family of Nature-based materials. Angewandte Chemie-International Edition. 2011;50:5438–66.
Himmel ME, Ding S-Y, Johnson DK, Adney WS, et al. Biomass recalcitrance: Engineering plants and enzymes for biofuels production. Science. 2007;315:804–7.
Chundawat SPS, Bellesia G, Uppugundla N, Sousa LD, et al. Restructuring the crystalline cellulose hydrogen bond network enhances Its depolymerization rate. J Am Chem Soc. 2011;133:11163–74.
Ding S-Y, Liu Y-S, Zeng Y, Himmel ME, et al. How does plant cell wall nanoscale architecture correlate with enzymatic digestibility? Science. 2012;338:1055–60.
Newman RH. Estimation of the relative proportions of cellulose I alpha and I beta in wood by carbon-13 NMR spectroscopy. Holzforschung. 1999;53:335–40.
Sturcova A, His I, Apperley DC, Sugiyama J, Jarvis MC. Structural details of crystalline cellulose from higher plants. Biomacromolecules. 2004;5:1333–9.
Wickholm K, Larsson PT, Iversen T. Assignment of non-crystalline forms in cellulose I by CP/MAS C-13 NMR spectroscopy. Carbohydr Res. 1998;312:123–9.
Fernandes AN, Thomas LH, Altaner CM, Callow P, et al. Nanostructure of cellulose microfibrils in spruce wood. Proc Natl Acad Sci U S A. 2011;108:E1195–203.
Jakob HF, Fengel D, Tschegg SE, Fratzl P. The elementary cellulose fibril in Picea abies: Comparison of transmission electron microscopy, small-angle X-ray scattering, and wide-angle X-ray scattering results. Macromolecules. 1995;28:8782–7.
Kennedy CJ, Cameron GJ, Sturcova A, Apperley DC, et al. Microfibril diameter in celery collenchyma cellulose: X-ray scattering and NMR evidence. Cellulose. 2007;14:235–46.
Newman RH, Hill SJ, Harris PJ. Wide-angle X-ray scattering and solid-state nuclear magnetic resonance data combined to test models for cellulose microfibrils in mung bean cell walls. Plant Physiol. 2013;163:1558–67.
Thomas LH, Altaner CM, Jarvis MC. Identifying multiple forms of lateral disorder in cellulose fibres. J Appl Crystallogr. 2013;46:972–9.
Thomas LH, Forsyth VT, Sturcova A, Kennedy CJ, et al. Structure of cellulose microfibrils in primary cell walls from collenchyma. Plant Physiol. 2013;161:465–76.
Xu P, Donaldson LA, Gergely ZR, Staehelin LA. Dual-axis electron tomography: a new approach for investigating the spatial organization of wood cellulose microfibrils. Wood Sci Technol. 2007;41:101–16.
Clair B, Almeras T, Pilate G, Jullien D, et al. Maturation stress generation in poplar tension wood studied by synchrotron radiation microdiffraction. Plant Physiol. 2011;155:562–70.
Moharir AV, Kiekens P. Cellulose crystallite sizes in diploid and tetraploid native cotton. J Appl Polym Sci. 1998;68:2107–12.
Ding SY, Himmel ME. The maize primary cell wall microfibril: A new model derived from direct visualization. J Agric Food Chem. 2006;54:597–606.
Newman RH, Redgwell RJ. Cell wall changes in ripening kiwifruit: C-13 solid state NMR characterisation of relatively rigid cell wall polymers. Carbohydr Polym. 2002;49:121–9.
Crow E, Murphy RJ. Microfibril orientation in differentiating and maturing fibre and parenchyma cell walls in culms of bamboo (Phyllostachys viridi-glaucescens (Carr.) Riv. & Riv.). Bot J Linn Soc. 2000;134:339–59.
Wang Y, Leppanen K, Andersson S, Serimaa R, et al. Studies on the nanostructure of the cell wall of bamboo using X-ray scattering. Wood Sci Technol. 2012;46:317–32.
Liu D, Song J, Anderson DP, Chang PR, Hua Y. Bamboo fiber and its reinforced composites: structure and properties. Cellulose. 2012;19:1449–80.
Lybeer B, Koch G. A topochemical and semiquantitative study of the lignification during ageing of bamboo culms (Phyllostachys viridiglaucescens). IAWA Journal. 2005;26:99–109.
Lybeer B, VanAcker J, Goetghebeur P. Variability in fibre and parenchyma cell walls of temperate and tropical bamboo culms of different ages. Wood Sci Technol. 2006;40:477–92.
Nishiyama Y, Langan P, Chanzy H. Crystal structure and hydrogen-bonding system in cellulose 1 beta from synchrotron X-ray and neutron fiber diffraction. J Am Chem Soc. 2002;124:9074–82.
Driemeier C, Santos WD, Buckeridge MS. Cellulose crystals in fibrovascular bundles of sugarcane culms: orientation, size, distortion, and variability. Cellulose. 2012;19:1507–15.
Dinand E, Chanzy H, Vignon MR. Suspensions of cellulose microfibrils from sugar beet pulp. Food Hydrocoll. 1999;13:275–83.
Zhang QS, Cheetamun R, Dhugga KS, Rafalski JA, et al. Spatial gradients in cell wall composition and transcriptional profiles along elongating maize internodes. BMC Plant Biol. 2014;14–27.
Slabaugh E, Davis JK, Haigler CH, Yingling YG, Zimmer J. Cellulose synthases: new insights from crystallography and modeling. Trends in Plant Science, 2014;14:99–106.
We thank the Institut Laue-Langevin for the award of neutron beamtime.
The authors declare no competing interests.
LHT carried out the X-ray scattering experiments, participated in the neutron scattering experiments and analysed much of the data. VTF supervised the running of the WANS experiments and data analysis. AM and IG supervised the running of the SANS experiments and data analysis. CMA participated in the interpretation of the results. MCJ carried out some of the data analysis and drafted the manuscript and all authors read and approved the final version.
About this article
Cite this article
Thomas, L.H., Forsyth, V.T., Martel, A. et al. Diffraction evidence for the structure of cellulose microfibrils in bamboo, a model for grass and cereal celluloses. BMC Plant Biol 15, 153 (2015) doi:10.1186/s12870-015-0538-x